Fe-Mn15.9Al4.2(wt.%)磁性塊材利用進行磁致伸縮實驗、動態機械分析儀與在外加磁場下利用共振頻率和阻尼分析儀量測楊氏係數及剪力模數。
Fe-Co19Ga17(at.%)磁性薄膜使用磁控濺鍍，主要以光學磁致伸縮計算薄膜之飽和磁致伸縮變化量、原子力顯微鏡與磁力顯微鏡觀察樣品表面與磁區分部與掃描式電子顯微鏡進行成份分析。
塊材與薄膜共同實驗儀器為X光繞射儀，最後再以震動式樣品磁力計觀察磁性質。

For Fe-Mn15.9Al4.2 (wt.%) magnetic bulk alloy, we used strain gauge to conduct magnetostrictive experiments. Mechanical properties were measured Young’s modulus and Shear modulus by Resonant Frequency & Damping Analyser under magnetic field and Dynamic Mechanical Analyzer.
We used magnetron sputtering to deposite Fe-Co19Ga17(at.%) thin films on Si(100) substrate. The amount of saturated magnetostriction was calculated by optical magnetostriction. The thin film’s topography and magnetic domain was observed by AFM and MFM. And it was analyzed components by SEM-EDS.
All of specimen’s structural property was investigated by X-ray diffraction and measured magnetic property by vibration sample magnetometer.

1.A. E. Clark, J. B. Restorff, M. Wun-Fogle, T. A. Lograsso, and D. L. Schlagel, Proceedings of the Intermag. Conf., Toronto, 2000.
2.Wu R Q. Origin of large magnetostriction in Fe-Ga alloys. J Appl phys, 2002,91:7358.
3.Cullen J R, A. E. Clark, M. Wun-Fogle,et al. Magnetoelasticity of Fe-Ga and Fe-Al alloys. J Magn Magn Mater, 2001, 226-230:948.
4.金重勳，磁性技術手冊，中華民國磁性技術協會出版 (2002)。
5.近角聰信著，張煦、李學養譯，“磁性物理學”，聯經出版事業公司 (1982)。
6.鄭振東，“實用磁性材料”，全華科技圖書股份有限公司（1999）。
7.王坤池，“超高真空中在Ge(111)面上成長Co超薄膜之退火效應及磁性現象研究”，國立台灣科技大學機研所碩士論文（2001）。
8.William F.Smith著，李春穎、許煙明、陳忠仁譯，“材料科學與工程”，高立圖書有限公司(1994)。
9.陳宿惠，“銀─鈷超薄膜在鉑（111）表面的磁性探討”，國立台灣師範大學物理所碩士論文（1999）。
10.陳淑貞，“鈷薄膜在矽(100)表面的磁性觀測”，國立台灣師範大學物理所碩士論文（1999）。
11.聶亨芸，“銀中介層對鈷超薄膜在鍺(111)基板上磁性質影響之研究”，國立清華大學材料科學工程研究所碩士論文(2002)。
12.陳元宗，“銥錳交換偶合之(鈷鐵棚/氧化鋁/鈷)磁穿隧元件的機械性、電性及磁性研究”，國立清華大學材料科學工程研究所博士論文 (2006)。
13.L. Mayer, J. Appl. Phys. 29, 1454 (1958).
14.D. Chen, G. N. Otto and F. M. Schimit, IEEE Tran on Magn., 9, 66 (1973).
15.Legvold et al., Phys. Rev. Lett., 10, 509 (1963).
16.A.E.Clark, et al., Phys. Rev., 138, A216 (1965).
17.J.Rhyne, et al., Phys.Rev., 138, A507 (1965).
18.賴耿陽，“應力應變的解析原理”，復漢出版社，pp. 24-59(1996)。
19.A.H.Morrish,“The physical principles of magnetism” (1965).
20.鍾文定，“鐵磁學”，(中冊)，科學出版社(1998)。
21.吳泰伯、許樹恩，“X光繞射原理與材料結構分析”，中國材料科學學會(1996)。
22.邱軍浩，“ Ti/C 元素對PrFeB 系複合奈米晶薄帶之磁性及交換藕合效應影響”國立中正大學物理研究所博士論文(2006)。
23.Model 7407 Vibrating Sample Magnetometer user’s manual, Lake Shore.
24.http://en.wikipedia.org/wiki/Vickers_hardness_test, 2015/6/23.
25.中研院金屬機械性質量測儀操作說明書(2015)。
26.ASTM E 1876-99, Am. Soc. Testing and Materials, (1999).
27.劉奇青，“鐵鎳鎵合金材料的鐵磁共振與磁彈性質研究”國立交通大學電子物理研究所博士論文(2013)。
28.G. Wastlbauer, and J.A.C. Bland, Advances in Physics 54, 137 (2005).
29.S. U. Jen, S. P. Wang, W. C. Chang, and H. W. Chang, Journal of Applied Physics, 112, 053904 (2012).
30.S. Chikazumi: Physics of Magnetism, Krieger, New York (1978).
31.R.E. Reed-Hill, “Physical Metallurgy Principle”, (1992).
32.E. George Dieter, Mechanical Metallurgy, SI Metric ed., 132 (1988)
33.K.H. Hwang, C.M. Wan, J.G. Byrne, Mat. Sci Eng. A, 132, 161 (1991).
34.P.M. Kelly. Trans. TMS-AIME, 233, 264 (1965).
35.W.D. Callister, Jr., Materials Science and Engineering an Introduction, 4th ed., pp.158-159.
36.莊達仁，“VLSI製造技術”，高立圖書有限公司 (2000)。
37.D. A. Porter and K. E. Easterling, “Phase Transformations in Metals and Alloys”, Chapman & Hall (1992).
38.V. K. Arkad’yev, J. Russ. Phys. –Chem. Soc. 44, 165 (1912).
39.N. Srisukhumbowornchai, S. Guruswany,J. Appl.Phys. 90,5680 (2001).
40.高銘南，國立海洋大學光電所碩士論文 (2001)。
41.S. Muller, P. Bayer, C. Reischl, K. Heinz, B. Feldmann, H. Zillgen, and M. Wuttig, Phys. Rev. Lett, 74, 765 (1995).
42.Software Koala V4 USER OPERATING MANUAL ,Lync´ee Tec SA,2009.
43.陳信廷，國立台灣科技大學機械研究所論文(2014)。
44.T.A. Lograsso, A.R. Ross, D.L. Schlagel, A.E. Clark, M. Wun-Fogle, Volume 350, Issues 1–2, 17 February 2003, Pages 95–101
45.陳柏邨，“鐵錳鋁合金的體心立方雙晶之研究”，國立台灣科技大學碩士論文 (2006)。
46.陳冠甫，“以方位影像顯微學分析鐵錳鋁合金的肥粒麻田散體、淬火雙晶與魏德曼組織”，國立台灣科技大學碩士論文 (2014)。