研究生: |
李明威 Ming-Wei Lee |
---|---|
論文名稱: |
矽溶膠灌漿液之材料性質和大地工程應用研究 Material Properties and Geotechnical Applications of Colloidal Silica Grout |
指導教授: |
廖洪鈞
Hung-Jiun Liao |
口試委員: |
鄭世豪
Shih-Hao Cheng 王錦伍 Jin-Wu Wang |
學位類別: |
碩士 Master |
系所名稱: |
工程學院 - 營建工程系 Department of Civil and Construction Engineering |
論文出版年: | 2018 |
畢業學年度: | 106 |
語文別: | 英文 |
論文頁數: | 131 |
中文關鍵詞: | 矽溶膠溶液 、砂土灌漿 、單壓強度 、土壤液化 |
外文關鍵詞: | colloidal silica grout, grouted sand, unconfined compressive strength, liquefaction |
相關次數: | 點閱:569 下載:1 |
分享至: |
查詢本校圖書館目錄 查詢臺灣博碩士論文知識加值系統 勘誤回報 |
本研究使用之矽溶膠灌漿液具耐久性和良好砂土灌注能力,雖具強鹼性(pH = 10),但膠凝後,膠體性質穩定。依本研究針對矽溶膠灌漿液之膠凝行為和膠凝後之強度性質試驗發現: 矽溶膠體強度隨二氧化矽和促凝劑濃度之增加而增加;在相同膠凝時間下,隨二氧化矽濃度增加,所需之促凝劑濃度會減少。此外,膠體強度和膠凝時間,也受溫度與砂土表面吸附粉末性質影響。雖然膠體強度不高,但因不具流動性,一旦充填砂土孔隙後,即足以防治土壤液化發生。在不同的灌漿砂試體準備方式下,因矽溶膠在砂土孔隙中分佈方式不同,會影響灌漿砂之強度和透水性質。其中,以攪拌方式準備之試體,因砂土顆粒接觸點間裹有漿液,所以其強度較以低壓灌注、而砂土顆粒接觸點間未有漿液之試體,高出約0 ~ 15%,兩者之差距隨膠體強度之增加而增加。比較以1.5倍和3倍砂土孔隙體積灌漿量注入之灌漿砂試體時,雖前者有少量氣泡存在孔隙間,但兩者之抗壓強度和透水性差距不大。雖前者較具經濟性,但若考量地層和地下水文之變異性,仍建議以3倍孔隙體積灌漿量進行抗液化土壤改作業為宜。
Colloidal silica grout was used in this study due to its good durability and injectability to sand. Although its pH value is high (=10), its gel is stable and has good durability under the groundwater table. Having done a series of laboratory tests on colloidal silica and its grouted sand, the findings can be presented as follows. The strength of colloidal silica grout increased with the concentration of silica and reagent in the grout. Under the same gel time, the higher the silica concentration in the grout, the lower the concentration of reagent is required. In addition, the strength and gel time of colloidal silica grout are also affected by the temperature and the adsorbed powder materials on the surface of sand particles. Although the strength of colloidal silica grout is not high, it is still capable to prevent the soil liquefaction from happening because of the non-liquid nature of the gel. Once it fully or partial fills the porosity of sand, sand will not be able to liquefy during earthquake. Furthermore, the properties of grouted sand are affected by the preparation methods of grouted sand. For example, the grouted sand specimens prepared by stirring mix method, the contact points between sand particles are coated with a thin layer of grout and bound the particles together. So a higher strength was obtained compared to those prepared by injection method which yields no grout coating at the particle contact points. The former shows a 0 ~ 15% higher strength than the latter. The difference in strength increases with increasing grout strength. Comparing the grouted sands prepared with 1.5 times and 3 times the porosity volume grout injection, there is some air bubbles in the pores of sand for the former. But the difference in the compressive strength and permeability between these two is not obvious. Finally, 1.5 times the porosity volume grout injection may seems to be more economic. But considering the changing nature of subsoil and groundwater conditions, it is still suggested that 3 times the porosity volume grout injection is more accountable for ground improvement against soil liquefaction.
參考文獻
1.ASTM D4320-84, (1984). Laboratory Preparation of Chemically Grouted Soil Specimen For Obtaining Design Strength Parameter.
2.Clough, G.W., Kuck, W.M. and Kasali, G. (1979). “Silicate-stabilized Sand”, Journal of Geotechnical Engineering Division, ASCE, Vol.105, No. GT1, pp. 65-82.
3.Liao, H.J., Huang, C.C., and Chao, B.S. (2003). “Liquefaction Resistance of a Colloid Silica Grouted Sand”, Proc. of 3rd International Conference on Grouting and Ground Treatment, New Orleans, pp. 1305-1313.
4.Schiffman, R.L. and William, C.R. (1958). “The Mechanical Behavior of Chemically Treated Granular Soil”, Proc. ASTM, Vol.58, pp. 1218-1244.
5.Skipp, B.O. and Penner, L. (1963). “The Improvement of Mechanical Properties of Sand”, Symposium or Organized by British National Society of the International Society of S.M.F.E. at the Institution of Civil Engineering held in May 1963.
6.Warner, J. (1972). “Strength Properties of Chemically Solidified Soil,” Journal of the Soil Mechanics and Foundation Diversion, ASCE, Vol.98, No. SM11, pp. 1163-1185.
7.Seed, H.B. and Idriss, I.M. (1971). “Simplified Procedure for Evaluating Soil Liquefaction Potential,” Journal of the Soil Mechanics and Foundation Diversion, ASCE, Vol. 97, No. SM9, pp. 1249-1273.
8.Ishibashi, I.M., Sherlif, M.A., and Cheng, W.L. (1982). “The Effects of Soil Parameters on Pore Pressure Rise and Liquefaction Prediction, ” Soils and Foundations, JSSMEF, Vol.22, No. 1, pp. 37-48
9.Tokimatsu, K. and Yoshimi, Y. (1982). “Criteria of Soil Liquefaction with SPT and Fines Content”. ASCE Proc. Conf. on Grouting in Geotech. Eng., New Orleans
10.Baker, W.H. (1982). “Planning and Performing Structural Chemical Grouting,” ASCE Proc. Conf. on Grouting in Geotech. Eng., New Orleans, pp. 515-539.
11.Head, K.H. (1982). Manual of soil laboratory testing, Volume 2 - Permeability shear strength and compressibility test, Wiley, New York
12.許峻銘,「以不同灌漿工法灌注恆久性灌漿材料之成效比較」,台灣科技大學營建工程所碩士論文,民國九十九年。
13.鄭毅傑,「變化灌漿材料和灌漿方式對不同土壤之改良強度影響」,台灣科技大學營建工程所碩士論文,民國九十八年。
14.林志誠,「地盤改良對黏土層島區式開挖行為之影響研究」,台灣科技大學營建工程所博士論文,民國九十六年。
15.黃啟瑞,「攪拌樁配置對軟弱黏土層島區開挖之影響」,台灣科技大學營建工程所碩士論文,民國九十四年。
16.祝惠美,「灌漿後土壤解壓行為之研究」,台灣科技大學營建工程所碩士論文,民國七十八年。
17.林摩西,「灌漿材料和待強化砂土對灌漿後砂土力學性質之影響」,台灣科技大學營建工程所碩士論文,民國七十七年。
18.林智偉,「無塑性細料對砂質土壤液化阻抗之研究」,成功大學土木工程研究所碩士論文,民國九十五年。
19.蘇勝豐,「水玻璃灌漿後砂土之力學特性研究」,淡江大學土木工程研究所碩士論文,民國七十五年。
20.廖洪鈞,「超微粒水泥/水玻璃之混合灌漿材料」,第二屆大地工程學術研討會論文專集,第141-150頁,民國七十六年四月。