研究生: |
黃新堯 Hsin-Yao Huang |
---|---|
論文名稱: |
奈米級核殼型橡膠添加劑、無機二氧化矽/有機高分子核殼型顆粒、及蒙特納石黏土對不飽和聚酯、乙烯基酯、及環氧樹脂之聚合固化反應動力、玻璃轉移溫度、体積收縮、機械性質及微觀型態結構之影響研究 Effects of nano-scale core-shell rubber additives, inorganic silica /organic polymer core-shell particle, and montmorillonite clay on the cure kinetics, glass transition temperatures, volume shrinkage, mechanical properties and cured sample morphology for unsaturated polyester, vinyl ester, and epoxy resins |
指導教授: |
黃延吉
Yan-Jyi Huang |
口試委員: |
陳崇賢
Chorng-Shyan Chern 邱文英 Wen-Yen Chiu |
學位類別: |
碩士 Master |
系所名稱: |
工程學院 - 化學工程系 Department of Chemical Engineering |
論文出版年: | 2012 |
畢業學年度: | 100 |
語文別: | 中文 |
論文頁數: | 327 |
中文關鍵詞: | 核殼形橡膠 、蒙特納石黏土 、不飽和聚酯 、乙烯基酯樹脂 、固化動力 、玻璃轉移溫度 、體積收縮 、機械性質 |
外文關鍵詞: | Core-Shell Rubber(CSR), Montmorillonite (MMT), unsaturated polyester(UP), vinyl ester resin (VER), curing kinetics, glass transition, volume shrinkage, microstructure, mechanical properties, radius of gyration |
相關次數: | 點閱:313 下載:2 |
分享至: |
查詢本校圖書館目錄 查詢臺灣博碩士論文知識加值系統 勘誤回報 |
本文目的主要為探討三種特用添加劑,分別為:(1)奈米級核殼型橡膠(core-shell rubber) (2)無機矽膠/有機高分子核殼型顆粒及(3)有機化改質蒙特納石黏土(Montmorillonite clay,MMT),其對苯乙烯/不飽和聚酯(或乙烯基酯)/特用添加劑三成份系統及環氧樹脂/硬化劑/特用添加劑三成份系統之反應前相容性,聚合固化反應動力,玻璃轉移溫度、微觀型態結構、抗體積收縮特性及機械性質等之影響研究。
本研究也利用小角度X-ray散射儀(SAXS)測量不飽和聚酯(UP)及乙烯基酯(VER)之稀薄苯乙烯(St)溶液之散射強度,再根據Guinier Law計算不同UP及乙烯基酯(VER)之環動半徑(Radius of Gyration),可用於St/UP(或VER)/MMT三成份系統,瞭解UP(或VER)分子擴散至蒙特納石黏土(MMT)層間之難易程度。
吾人也利用微分掃描熱分析儀(DSC)及傅立葉轉換紅外光譜儀(FTIR)測量ST/UP(or VER)/additive 三成份系在聚合固化中之反應動力。最後依據Takayanagi機械模式,ST/UP(or VER)/additive三成份系聚合固化後的樣品,其在各相區之玻璃轉移溫度,吾人亦以動態機械測定儀(DMA)測量之
The effects of four additives, including (1) nano- scale core-shell rubber additive,(2) inorganic silica gel/organic polymer core-shell particle, (3) organic montmorillonite clay, on the cure kinetics, glass transition temperatures, cured sample morphology, volume shrinkage characteristics and mechanical properties of the Styrene(St)/ Unsaturated polyester (or Vinyl ester resin)/ additives ternary systems and Epoxy/curing agent /additive ternary systems after the cure have been investigated.
The experimental results have been explained by integrated measurements combining phase characteristic of the St/VER/additive ternary system and Epoxy/curing agent /additive ternary systems before the cure, final cure conversion, glass transition temperature, SAXS and WAXS analysis, cured sample morphology and Mechanical properties.
Also the scattering intensity of vinyl ester resin (VER) and unsaturated polyester (UP) with different structure in dilute styrene solution was measured by the method of small angle X-ray scattering (SAXS), and the radius of gyration of VER and the UP molecule can then be calculated by using the Guinier law.
The reaction kinetics for the ST/UP(or VER)/additive ternary system during the cure was measured by differential scanning calorimetry(DSC) and Fourier transform infrared spectrometry (FTIR). Finally, based on the Takayanagi mechanical models, the glass transition temperature in each region of the cured samples for ST/UP(or VER)/additive ternary system has been measured by dynamic mechanical analysis (DMA).
1. R.B. Burn, Polyester Molding Compounds,Marcel Dekker, Inc, New York, 1982.
2. Bryan Ellis. Chemistry and Technology of Epoxy Resin. 1993, London: Blackie Academic & Professional.
3. 陳東課, 環氧樹脂在積層板之應用,化工技術第四卷第五期, 1996.
4. 賴耿陽, 環氧樹脂應用實務, 復漢出版社,台灣, 1999.
5. 賴家聲, 環氧樹脂與硬化劑(上) ,復漢出版社,台灣(1999).
6. S. V. Levchik, G. Camino, M. P. Luda, L. Costa, G. Mullerm, and B. Costes, Polym. Deg. Stab., 1998. 60, 169.
7. 黃滄閔, 碩士論文,成功大學, 2001.
8. R.E. Young, in “Unsaturated Polyester Technology,“ ed. P.F. Bruins, Gordon and Breach Science Publishers, New York , 1976.
9. M.E. Kelly, in “Unsaturated Polyester Technology,“ ed. P.F. Bruins, Gordon and Breach Science Publishers, New York , 1976, 370.
10. F. Fekete, “Unsaturated Polyester Technology,“ ed. P.F. Bruins, Gordon and Breach Science Publishers, New York , 1976, 28.
11. E. Martuscelli, P. Musto, G.. Ragosta, G. Scarinzi, and E. Bertotti, J.Polym.Sci., Part B:Polym.Phys., 1993. 31, 619.
12. S.B. Pandit and V.M. Nadkarni, Ind. Eng. Chem Res., 1994. 33, 2778.
13. The B.F. Goodrich Co. WO93/21274 Oct. 28,1993.
14. Crc for Polymers Pty. Ltd., WO97/43339 Nov. 20,1997.
15. 吳嘉鴻, 碩士論文,台灣科技大學, 2003.
16. 黃俊翰, 碩士論文,台灣科技大學, 2009.
16a. 戴孟祥, 碩士論文,台灣科技大學, 2009
17. 陳曉蘭, 碩士論文,台灣科技大學, 2010.
18. 許毓倫, 碩士論文,台灣科技大學, 2011.
19. E.J. Bartkus and C.H Kroekel, Appl.Polym.Symp., 1970. 15, 113.
20. K.E.Atkins, in”Sheet Molding Compound :Science and Technology”Ed., H.G. Kia, Hanser Publishers, New York , 1993. Ch4.
21. V.A. Pattison, R.R. Hindersinn, and W.T. Schwartz,J. , Appl.Polym.Sci., 1974. 18, 2763.
22. V.A. Pattison, R.R. Hindersinn, and W.T. Schwartz,J. , Appl.Polym.Sci., 1975. 19, 3045.
23. L. Suspene, D. Fourquier, and Y. S. Yang, Polymer, 1991. 32, 1593.
24. Y. J. Huang and C. M. Liang, Polymer, 1996. 37, 401.
25. L. J. Lee, W. Li , and K.H. Hsu, Polymer, 2000. 41, 711.
26. C.B. Bucknall, I.K. Partridge, and M.J. Phillips, Polymer, 1991. 32, 636.
27. Y. J. Huang, T. S. Chen, J. G. Huang, and F. H. Lee, J. Appl. Polym. Sci., 2003. 89, 3336.
28. J.P. Dong , J.H. Lee , D.H. Laiand, and Y. J. Huang, Appl. Polym.Sci., 2005. 98, 264.
29. C.P. Hsu, M. Kinkelaar, P. Hu, and L.J. Lee., Polym.Eng.Sci., 1991. 31, 1450.
30. Y.J. Huang, C.J. Chu, and J.P. Dong, J. Appl. Polym. Sci., 2000. 78, 543.
31. Y.J. Huang and C.C. Su, J. Appl. Polym. Sci., 1995. 55, 323.
32. J.P. Dong, J.G. Huang, F.H. Lee, J.W. Roan and Y.J. Huang, J.Appl.Polym.Sci., 2004. 91, 3388.
33. Y.J. Huang and W.C. Jiang, Polymer, 1998. 39, 6631.
34. B. M. Novak, Adv. Mater., 1993. 5, 422.
35. X. Kornmann, L. A. Berghund, J. Sterte, and E. P. Giannelis, Polym. Eng. Sci., 1998. 38, 1351.
36. Y. Kojima, A. Usuki, M. Kawasumi, A. Okada, T. Kurauchi, and Kamigaito, J.Polym.Sci. Part A: Polym.Chem, 1993. 31, 983.
37. E. P. Giannelis, Adv. Mater., 1996. 8, 29.
38. A. Usuki, Y. Kojima, M. Kawasumi, A. Okada, A. Fujushima, T. Kurauchi, and O. Kamigaito, J. Mater. Res., 1993. 8, 1179.
39. P. B. Messersmith and E. P. Giannelis, Chem. Mater., 1994. 6, 1719.
40. W. Gilman and T. Kashiwagi, SAMPE Journal, 1997. 33, 42.
41. R.J. Roe, Methods of X-ray and Neutron Scattering in Polymer Science, Oxford University Press, New York, 2000. Ch5.
42. 盧天智, 碩士論文,台灣科技大學, 1991.
43. H.R. Allcock and F.W. Lampe, ”Contemporary Polymer Chemistry”, 3rd Ed., Prentice Hall, Englewood Cliffs, 2003, 59.
44. Y.S. Yang and L.J. Lee, Polymer, 1988. 29, 1793.
45. K. Horie, I. Mita, and H. Kambe, J.Polym.Sci.PartA-1:Polym. Chem., 1969. 7, 2561.
46. 江文慶, 碩士論文,台灣科技大學, 1996.
47. Y.J. Huang and C.C. Su, J. Appl. Polym. Sci., 1995. 55, 305.
48. Y.J. Huang and J.C. Horng, Polymer, 1998. 39, 3683.
49. Y.J. Huang and L.D. Chen, Polymer, 1998. 39, 7049.
50. 蘇進成, 碩士論文,台灣科技大學, 1992.
51. 林立翔, 碩士論文,台灣科技大學, 1992.
52. Y.J. Huang and C.C. Su, Polymer, 1994. 35, 2397.
53. Y.J. Huang, T.J. Lu, and W. Hwu, Polym. Eng. Sci., 1993. 33, 1.
54. C.B. Bucknall, I.K. Partridge, and M.J. Phillips, Polymer, 1991. 32, 786.
55. T. Mitani, H. Shiraishi, K. Honda, and G.E. Owen, 44th Annual Conference Composite Institute,SPI,Session 12-F, 1989.
56. W.D. Cook and O. Delatycki, J.Polym.Sci.,Polym.Phys.Ed., 1974. 12, 2111.
57. W.D. Cook and O. Delatycki, J.Polym.Sci.,Polym.Phys.Ed., 1974. 12, 1925.
58. Y.J. Huang, S.C. Lee, and J.P. Dong, J. Appl. Polym. Sci., 2000. 78, 558.
59. Y.J. Huang, T.S. Chen, J.G. Huang, and F.H. Lee, J.Appl.Polym.Sci., 2003. 89, 3347.
60. D.S. Kim, K. Cho, J.H. An, and C.E. Park, J. Mater. Sci., 1994. 29, 1854.
61. J.S. Ullett and R.P. Chartoff, Polym. Eng. Sci., 1995. 35, 1086.
62. M. Abbate, E. Martuscelli, P. Musto, G. Ragosta, and G. Scarinzi, J.Appl. Polym. Sci., 1995. 58, 1825.
63. M.L.L. Maspochand and A.B. Matinez, Polym.Eng. Sci., 1998. 38, 290.
64. N. A. Miller and C. D. Stirling, Polym. Comps., 2001. 9, 31.
65. K. F. Lin and Y.D. Shieh, J. Appl. Polym. Sci., 1998. 69, 2069.
66. K.F. Lin and Y.D. Shieh, J. Appl. Polym. Sci., 1998. 70, 2313.
67. P. Hazot, C. Pichot, and A. Maazouz,, Macromol Chem. Phys., 2000. 201, 632.
68. B.J.P. Jansen, S. Rastogi, H.E.H. Meijer, and P.J.Lemstra, Macromolecules, 2001. 34, 3998.
69. H.J. Sue, E.I. Garciameitin, and D.M. Picklman, in Polymer Toughening, Ch. 5, ed., C.B. Arends, Marcel Dekker, 1996.
70. The Dow Chemical Company US Patent 4,778,851 Oct. 18 1998.
71. J.Y. Qian, R.A.Pearson, V.L. Dimonie, and M.S. El-Aasser, J. Appl. Polym. Sci., 1995. 58, 439.
72. D. J. Suh, Y. T. Lim, and O. O. Park, Polymer, 2000. 41, 8557.
73. R. K. Bharadwaj, A. R. Mehrabi, C. Hamilton, C. Trujillo, M. Murga, R. Fun, A. Chavira, and A. K. Thompsor, Polymer, 2002. 43, 3669.
74. The Dow Chemical Company US Patent 6,287,922 Sep.11, 2001.
75. A. Al-khanabashi, M. El-Gamal, and A. Moet, J. Appl. Polym. Sci., 2005. 98, 767.
76. 梁繼文, 礦物學(下), 1984.
77. T. Lan and T.J Dinnavaia, Chem. Mater, 1994. 6, 2216.
78. J. Chiefare, Y. K. Chong, F. Ercole, J. Krstina, J. Jefery, T. P. T. Le, R. T. A. Mayadunne, G. F. Meijs, C. L. Moad, G. Moad, E. Rizzardo, and S. H. Thong, Macromolecules, 1998. 31, 5559
79. P.Takolpuckdee, C. A.Mars, and S.Perrier, Org. Lett., 2005. 7, 3449.
80. Y.Tsujii, M.Ejaz, K.Sato, A.Goto, and T.Fukuda, Macromolecules, 2001. 34, 8872.
81. D.L.Patton and R.C.Advincula, Macromolecules, 2006. 39, 8674.
82. R.Narain and S.P.Armes, Macromolecules, 2003. 36, 4675.
83. M. H.Stenzel, T. P.Davis, and A. G.Fane, J Mater Chem, 2003. 13, 2090.
84.M.R. Kamal, S. Slurour.,and M. Ryan, SPE. ANTEC Papers. 19, 187
(1973).
85. S.Y. Pusatcioglu, A.L.Fricke., and J.C. Hasseler, J. Appl. Polym. Sci., 24, 937 (1979).
86. C. D. Han, and K. W. Lem, J. Appl. Polym. Sci., 28, 749 (1983).
87. J. F. Stevenson, Polym. Eng. Sci., 26(11), 746 (1989).
88. J. F. Stevenson, SPE. ANTEC. Papers, 26, 452(1980).
89. L. J. Lee, Polym. Eng. Sci., 21, 483 (1981)
90. Y. J. Huang, and L. J. Lee, AICHE. J., 31, 1585(1985).
91. C. D. Han, and D. S. Lee, J. Appl. Polym. Sci., 37, 2859 (1987).
92. C. S. Chern, and D. C. Sundberg, ACS. Polym. PREP, 26(1), 296
(1985).
93. G. L. Batch, and C. W. Mocosko, SPE. ANTEC Paper, 974(1987).
94. Y. J. Huang, J. D. Fan, and L. J. Lee, Polym. Eng. Sci., 30(11), 684
(1990)
95. 陳彥廷, 碩士論文,台灣科技大學, 2012.
96. Patrick W. K. Lam, Polym. Eng. Sci., 1989. 29(10), 690-698.
97. K.Horie, I Mita, and H.Kambe, J. Polym. Sci. : Part A1: Polymer Physics, 1970, 2839.
98. S. L. Rosen, Fundamental Principles of Polymeric Materials, 2ed, Wiley, New York, 1993, 321-337.
99. J. Als-Nielsen and D. McMorrow, Elements of Modern X-ray Physics, Wiley, New York, 2001.
100.B.D Cullity, Elements of X-ray Diffraction. 2nd Ed, Addison-wesley, Reading, MA, 1978.
101.L.H. Sperling, Introduction to Physical Polymer Science, 3rd Ed., 2001, 85~90.
102.J. Madejova, Vib. Spectgrosc.2003, 31, 1.
103.F. Rouessac, and A. Rouessac, Chemical Analysis: Modern Instrumentation Methods and Techniques, 2nd Ed., Wiley, New York, 2007, p. 228.
104.D.C. Harris, Quantitative Chemical Analysis, 8th Ed., W.H. Freeman and Company, New York, 2010, Chap. 9.
105.http://www.zirchrom.com/organic.htm, Dissociation Constants of Organic Acids and Bases.
106.J.W. Robinson, E.M.S. Frame, and G.M. Frame II, Undergraduate Instrumental Analysis, 6th Ed., Marcel Dekker, New York, 2005, p. 227-279.
107.B. Stuart, Infrared Spectroscopy: Fundamentals and Applications, Wiley, New York, 2004, p. 72 and p.77.
108.郭庭蓁, 碩士論文 台灣科技大學, 2006.
109.M. Takayanagi, K. Emada, and T. Kajiyama, J. Polym. Sci. Part C, 1966. 15, 263.
110. Jiwon Choi, Jason Harcup, Albert F. Yee, Quan Zhu, and Richard M. Laine, J. Am. Chem. Soc., 2001. 123, 11420-11430.