本研究以物理方式產生泡沫，再將泡沫與水泥飛灰漿或鹼激發爐灰漿均勻拌合，分別製成水泥基泡沫漿體與鹼激發爐灰泡沫漿體，並使用水泥基漿體添加保麗龍球製成保麗龍混凝土，三種輕質混凝土交叉比較。輕質混凝土以新拌單位重600、800及1000 kg/m3為設計標準，進行物理性質試驗(新拌單位重、流度質、抗壓強度、吸水率、熱傳導係數、吸音值、長度變化量、耐火性)，最後根據各種配比進行成本的計算與分析。研究結果顯示:添加泡沫與保麗龍球降低混凝土單位重的同時，流度值、抗壓強度、熱傳導係數降低，吸音係數、吸水率、長度變化量與耐火試體背面溫度提高，輕質混凝土流度值介於20~135%之間，28天齡期抗壓強度在4.49~70.3 kgf/cm2之間，熱傳導係數0.06~0.24 W/m.K，吸音係數介於0.29~0.78，耐火性皆屬於A級防火門材料。並考量成本、碳排放量分析後以編號G8為最佳配比。

This study is using foam agent to produce foam by foaming machine. And then mixing foam and pozzolanic cement paste or Alkali-activated paste together. Expanded Polystyrene (EPS) is also used to combine pozzolanic cement. In each unit weight (600, 800, 1000 kg/m3), three kinds light weight concrete were compared. Experiments conducted were fresh unit weight, flow ability, compressive strength, absorption capacity, shrinkage, thermal conductivity, absorption coefficient and fire resistance test. The results show that the addition of foam or EPS will reduce unit weight, the similar time flow, compressive strength and thermal conductivity as well as increasing absorption coefficient, absorption capacity, shrinkage and specimen temperature of fire resistance. After considering the costs and carbon emissions, group G8 is the best.

1.邱軍付、羅淑湘、魯虹、孫桂芬、王永魁，「大摻量粉煤灰超輕泡沫混凝土的試驗研究」，新型建築材料，第一期，第74-77頁(2013)。
2.劉陽、王晴、許峰，「泡沫混凝土的製備及多功能性」，混凝土，第278期，第120-121頁(2012)。
3.袁俊，「粉煤灰泡沫混凝土屋面材料的研究」，水泥工程，第四期，第82-84頁(2010)。
4.徐開勝，「泡沫混凝土的發展及應用」，四川建材，第四期第38卷，第28-29頁(2012)。
5.王君明，「輕質混凝土在房屋建築中的應用探析」，金壇市城鄉和住房建設委員會(2013)。
6.顏聰，土木材料，台中 (2006)。
7.Valore, R.C., ”Cellular concrete part 1 composition and methods of production”, ACI 50:pp. 773-796(1954).
8.Alexanderson, J., “Relations between structure and mechanical properties of autoclaved concrete”, Cement and Concrete Research, Vol. 9, Issue 4, pp. 507-514, July (1979).
9.Gorgiades, A., Ftikos, C., Marinos, J. “Effect of microspore structure on autoclaved aerated concrete shrinkage”, Cement and concrete research, Vol. 21, Issue 4, pp.655-662, July( 1991).
10. Nambiar, E.K., Kunhanandan, Ranmamurthy, K., “Influence of filler type on the properties of foam concrete”, Cement and Concrete Composites, Vol. 28, pp. 475-480(2006).
11.劉佳奇、霍冀川、雷永林、李嫻等人，「發泡劑及泡沫混凝土的研究進展」，化學工業與工程，第27卷，第一期(2010)。
12.閏振甲，「泡沫混凝土有望成為保溫材料首選」，混凝土世界，No.7 第22-26頁(2010)。
13.李靖山、李碩，「輕質泡沫混凝土在建築節能保溫中的應用現狀與前景」，中國科技縱橫，第1期(2014)。
14.行政院環境保護署，噪音原理/防制材料使用手冊，2010。
15.周明杰、王娜娜、趙曉艷、趙曉輝，「泡沫混凝土的研究和應用最新進展」，混凝土，第四期(2009)。
16.潘志華、陳國瑞、李東旭，「現澆泡沫混凝土常見品質問題分析及對策」，新型建築材料，第31卷，第一期，第 4-7頁(2004)。
17.汪琦，「蒸壓加氣混凝土氣體裂縫現象的剖析及防治」，廣東省惠州市會城區規劃建設局，廣東建材第7期(2006年)。
18.王蕊，「我國加氣混凝土制品應用現狀及其前景」，齊齊哈爾宏宇建築工程質量檢測有限責任公司，科技創業家，No.12(2012)。
19.Cook, D.J., “Expanded polystyrene beads as lightweight aggregate for concrete“, (1973).
20.Cook, D.J., “New Concrete Materials”, Surrey University Press, London”, (1983).
21.Perry, S.H., Bischoff, P.H., Yamura, K., “Mix details and Material behavior of polystyrene aggregate concrete”,(1991).
22.Bagon, C., Frondistou, Yannas, “Marine floating concrete made with polystyrene beads”, (1976).
23.Bischoff, P.H., “Polystyrene aggregate concrete subjected to hard impact”, (1990)。
24.Sussman, V., “Lightweight plastic - aggregate concrete”, 1975.
25.Ganesh, K., Babu, D., Saradhi, Babu, “Behavior of lightweight expanded polystyrene concrete containing silica fume”, 2003.
26.陳兵、陳龍珠，「EPS輕質混凝土力學性能研究」，第三期 (2004)。
27.劉嫄春、張令心、戰佳朋、蔡玉超，「EPS輕質混凝土強度模型」，理論研究，第2期 (2013)。
28.谷亞新、王延釗、王小萌，「不同工藝泡沫混凝土的研究進展」，混凝土，第十二期 (2013)。
29.甘戈金、趙晚群，「混凝土發泡劑的研究進展」，中國硅酸鹽學會，混凝土與水泥製品學術討論會 (2013)。
30.丁起，「新型高效混凝土發泡劑的研究」，新型建築材料，第16-18頁(2009)。
31.SavoIy, A., “Foaming agent composition and process”,US5714001, Feb.3 (1998).
32.Sommer, A., “Foaming agent for making cellular and concrete and method of making same”, US3141857 JuIy 21.
33.Duxson, P., Provis,J. L., “Designing Precursors for Geopolymer Cement ”,journal of the American Ceramic Society, vol. 91, no12, pp.3864-3869 (2008).
34.Purdon, A.O., ”The action of alkalis on blast furnace slag”,Journal of the Society of Chemical Indusrty, vol. 59, no. 9, pp.191-202 (1940).
35.Glukhovsky, V.D., Rostovskaja, G.S., Rumyna, G.V., ”High strength slag alkaline cement ”, pp. 164-168.
36.楊南如，「鹼膠凝材料形成的物理化學基礎(I)」，矽酸鹽學報，Vol.24，No.2April， pp.209-215，北京 (1996)。
37.黃兆龍，「混凝土性質與行為」，詹氏書局，(台北) 2002。
38.蒲心誠、楊長輝，「高強鹼爐渣(JK)流態混凝土研究」，混凝土，第18-30頁(1994)。
39.Wang, S.-D. and Scrivener, K.L., “Hydration products of alkali activated slag cement,”Cement and Concrete Research,vol.25,no.3,pp561-571,4//,1995.
40.劉凌江，「用增鈣粉煤灰作水泥混合材的研究」，粉煤灰綜合利用vol. 2:46-47 (1997)。
41.Palomo, A., Grutzeck, M.W., Blanco, M. T. “Alkali-activated fly ashes. A cement for the future.”, Cement and Concrete Research,29:1323-1329., 1999.
42.Puertas, F., S Martinez-Ramirez, Alonso,S., Vazquez, T., “Alkali-activated fly ash/slag cements: Strength Behavior and hydration products”, Cement and Concrete Research, Volume 30, Issue 10, October, pages 1625-1632, 2000.
43.Xu, H., Van Deventer, J.S.J., “The geopolymerisation of alumino-silicate minerals”, vol. 59，Issue 3, Pages247-266, 2000.
44.Swamy, R.N., “Al-asali,Engineering properties of concrete affected by alkali-silica reaction”,ACI Materials Journal 85, vol.5pp.367-374, 1988.
45.Della M Roy, “Alkali-activated Cements Opportunities and challenges”, Cement and Concrete Research, vol.29, pp.249-254, 1999.
46.Li, C., Sun, H. and Li, L., “A review:The comparison between alkali-activated slag(Si+Ca) and metakaolin (Si+Al)cements,”Cement and Concrete Research ,vol.40,no.9,pp1341-1349,9//,2010.
47.焦寶祥，水玻璃-礦渣水泥的緩凝劑研究，新型建築材料，2002。
48.趙偉、朱琦、曾金雄，「粉煤灰-水泥基泡沫混凝土性能的試驗研究」，四川建材，第四期，2010。
49.Pachwco, F. T., Castro, J. G., ”Alkali-activated binders: A review: Part 1. Historical background, terminology, reaction mechanisms and hydration products”, Construction and Building Materials, vol. 22, no. 7, pp. 1305-1314(2008).
50.Sun, W., Zhang, Y.S., Lin, W. and Lui, Z.Y., “In situ monitoring of the hydration process of K-PS geopolymer cement with ESEM”,Cement and Concrete Research, vol. 34, pp.935-940 (2004).
51.Barbosa, V.F.F., Mackenzie, K.J.D. and Thaumaturgo, C., “Synthesis and characterisation of materials based on inorganic polymers of alumina and silica : sodium polysialate polymers”, International Journal of Inorganic Materials, vol. 2, pp. 309-317 (2000).
52.陳兵、涂思炎、翁友法，「EPS輕質混凝土性能研究」，建築材料學報，Vol.10 No.1，2007。
53.Ozicik,M.N, 「熱傳導學」，國立編譯館主編，1984。
54.吳佳銘，「含再生綠建材低噪音鋪面績效評估及噪音預測模式建立之研究」，國立台灣科技大學，博士論文，2007。
55.張柏成譯著，噪音控制之原理與實務，徐氏基金會，台北，1987。
56.行政院環境保護署，噪音/防制材料使用手冊，http://ncs.epa.gov.tw/DD/DD06/990107_1.pdf（2010）。
57.黃兆龍，高等混凝土技術，課堂講義，pages252-255。
58.葉韋廷，「添加椰殼纖維與水庫淤泥對無機聚合物性質影響之探討」，台灣科技大學，碩士論文，2014。
59.林志忠，「公共工程使用再生材料落實節能減碳初步探討」，國立中央大學，碩士論文，2011。
60.Benjamin, C. M., Ross, P. W., Janine, L., Arie V. R., Glan, D. C.,”Costs and carbon emissions for geopolymer pastes in comparison to ordinary Portland cement”, Journal of Cleaner Production, vol. 19, pp.1080-1090(2011).
61.中華民國保麗龍回收再生協會，http://www.ctepsra.org.tw/index.php/packing-styrofoam/49-2013-05-10
62.Chen, G. D., Henderson, D. ,”Ototoxicity of styrene”, Journal of Otology, vol. 6, Issue 2, pp. 1-9(2011).